HumiSeal 1B73EPA is a fast drying, single component, acrylic conformal coating intended for use on printed circuit assemblies. HumiSeal? 1B73EPA demonstrates excellent flexibility, fluoresces under UV light for ease of inspection and is easily repaired. HumiSeal? 1B73EPA coating is MIL-I-46058C qualified, IPC-CC-830, RoHS Directive 2002/95/EC and EPA 33/50 compliant, and recognized under UL File Number E105698.

Cleanliness of the substrate is of extreme importance for the successful application of a conformal coating. Surfaces must be free of moisture, dirt, wax, grease, flux residues and all other contaminants. Contamination under the coating could cause problems that may lead to assembly failures.

Depending on the complexity, density and configuration of components on the assembly, it may be necessary to reduce the viscosity of HumiSeal? 1B73EPA with HumiSeal? Thinner 600 in order to obtain a uniform film. Once optimum viscosity is determined, a controlled rate of immersion and withdrawal (5-15 cm/min) will further ensure even deposition of the coating and ultimately a uniform film. During the application, evaporation of solvent causes an increase in viscosity that should be adjusted by adding small amounts of HumiSeal? Thinner 600. Viscosity in the dip tank should be checked regularly, using a simple measuring device such as a Zahn or Ford viscosity cup.

HumiSeal? 1B73EPA can be sprayed using conventional spraying equipment. Spraying should be done in an environment with adequate ventilation so that the vapour and mist are carried away from the operator. The addition of HumiSeal? Thinner 600 is necessary to ensure a uniform spray pattern resulting in pinhole-free film. The amount of thinner and spray pressure will depend on the specific type of spray equipment used and operator technique. The recommended ratio of HumiSeal? 1B73EPA to HumiSeal? Thinner 600 is 1:1 by volume; however the ratio may need to be adjusted to obtain a uniform coating.

HumiSeal? 1B73EPA may be brushed with a small addition of HumiSeal? Thinner 600. Uniformity of the film depends on component density and operator’s technique.

Product Specification

Product Specification
Density, per ASTM D147596 ± .03 g/cm3
Solids Content, % by weight per Fed-Std-141, Meth. 404423 ± 3 %
Viscosity, per Fed-Std-141, Meth. 4287230 ± 30 centipoise
VOC739 grams/litre
Drying Time to Handle per Fed-Std-141, Meth. 406130 minutes
Recommended Coating Thickness25 – 75 microns
Recommended Curing Conditions24 hrs @ RT or 60 min. @ 76°C
Time Required to Reach Optimum Properties7 days
Recommended ThinnerHumiSeal? Thinner 600
Recommended StripperHumiSeal? Stripper 1080
Shelf Life at Room Temperature, DOM24 months
Thermal Shock, 50 cycles per MIL-I-46058C-65°C to 125°C
Coefficient of Thermal Expansion – TMA67 ppm /°C
Glass Transition Temperature – DSC42°C
Modulus – DMA11.1 MPa
Flammability, per UL 94V-0
Dielectric Withstand Voltage, per MIL-I-46058C>1500 volts
Dielectric Breakdown Voltage, per ASTM D1496300 volts
Dielectric Constant, at 1MHz and 25°C, per ASTM D150-982.6
Dissipation Factor, at 1MHz and 25°C, per ASTM D150-980.01
Insulation Resistance, per MIL-I-46058C5.5 x 1014ohms (550TΩ)
Moisture Insulation Resistance, per MIL-I-46058C7.0 x 1010 ohms (70GΩ)
Fungus Resistance, per ASTM G21Passes